The main components of chrome corundum are Al2O3 and Cr2O3, which form a continuous solid solution. According to the Al2O3-Cr2O3 binary phase diagram, adding Cr2O3 to Al2O3 single-phase material not only does not reduce the refractoriness of the material, but the refractoriness increases with the increase of Cr2O3 Conteúdo .
Adding Cr2O3 to the corundum material, as the temperature rises, Al2O3 and Cr2O3 gradually form a solid solution, so that the corundum particles and the matrix are closely combined, and further form a ring-shaped solid solution belt on the surface of the corundum particles, so that the material is closely combined between particles and particles, and between particles and fine powder at high temperatures, and the bonding phase is an aluminum-chromium Fase de solução sólida com um alto ponto de fusão . Mesmo em altas temperaturas, ele ainda mantém a força de ligação, portanto, os materiais refratários de corundos cromados têm fortes propriedades mecânicas à temperatura ambiente e propriedades mecânicas de alta temperatura .
O CR2O3 é um componente de alta qualidade dos materiais refratários e pode formar compostos de alto ponto de fusão com uma variedade de óxidos ., por exemplo, Cr2O3 e Al2O3 podem formar uma solução sólida contínua, cujo ponto de fusão está acima de 2050 graus; Cr2O3 e MGO/FEO formam alto ponto de fusão de magnésio spinel/espinélio de ferro cromo; Cr2O3 e Cu2O podem formar um composto com um ponto de fusão acima de 1600 graus; A temperatura de fusão da baixa eutética formada por CR2O3 e SiO2 atinge 1720 graus; etc .
Além disso, o CR2O3 também pode aumentar a viscosidade da escória, e o aumento da viscosidade da escória pode desacelerar a taxa de penetração da escória no refratário . em resumo, o Cr2O3 pode melhorar a resistência à erosão da escória e a resistência ao refratário.